Heat treated: 1653°C - 1641°C.
35JN210 Mechanical
| Yield Rp0.2 (MPa) | Tensile Rm (MPa) | Impact KV/Ku (J) | Elongation A (%) | Reduction in cross section on fracture Z (%) | As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 369 (≥) | 621 (≥) | 14 | 32 | 31 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 232 |
35JN210 Physical
| Temperature (°C) | Modulus of elasticity (GPa) | Mean coefficient of thermal expansion 10-6/(°C) between 20(°C) and | Thermal conductivity (W/m·°C) | Specific thermal capacity (J/kg·°C) | Specific electrical resistivity (Ω mm²/m) | Density (kg/dm³) | Poisson’s coefficient, ν |
|---|---|---|---|---|---|---|---|
| 43 | - | - | 0.31 | - | |||
| 185 | 773 | - | 44.3 | 412 | - | ||
| 891 | - | 11 | 13.2 | 441 | 324 |
Grain oriented steel is 3% silicon-iron alloys developed with a grain orientation to provide very low power loss and high permeability in the rolling direction, for high efficiency transformers.