B35A250 Non Grain Oriented Electrical steel
For B35A250 steel, the magnetic induction strength is mainly related to the silicon content and crystal structure.
B35A250 steel is a soft magnetic alloy silicon iron with very low carbon content. The addition of silicon to electrical steel mainly increases the resistivity and maximum magnetic permeability of iron, reduces coercivity, core loss (iron loss) and magnetic aging.
B35A250 steel is coated with inorganic salt or semi-organic salt insulating film on the surface, which can improve the filling factor of the core, adhesion of the surface insulating film, heat resistance, corrosion resistance, rust resistance, good weldability, and good flushability.
B35A250 steel Mechanical Properties
|
Grade |
Nominal thickness（mm） |
tensile strength L（N/mm2） |
Yield Strength L（N/mm2） |
Elongation L（%） |
Hardness HV1 |
Bending frequency (times) |
Stacking factor（%） |
|
B35A250 |
0.35 |
7.60 |
549 |
429 |
20 |
217 |
≥5 |
B35A250 steel sheet/plate Electromagnetic induction standar
|
Grade |
Nominal thickness（mm） |
Theoretical density（kg/dm3） |
Maximum core loss P17/50 |
minimum magnetic induction（T） |
|
B35A250 |
0.35 |
7.60 |
2.50 |
1.62 |
Hot Tags: b35a250 non grain oriented electrical steel, China, suppliers, manufacturers, factory, buy, price, pricelist, for sale, in stock, free sample, uniform color, high permeability, Silicon steel coil, igh magnetic susceptibility, Coated, reduce hysteresis loss