410 ROUND BARS can be categorically said that steel bars are one of the core components of any manufacturing industry or for that matter any industry that relies on machineries. versatile applications in automotive, textile, fabrication, construction, cement, ship building, paper and pulp, defence, heavy earth moving equipments or aerospace.
ASTM A276 410 Stainless Steel Round, Bright, Hex, Threaded Bar Chemical Composition
The chemical composition of grade Stainless Steel 410 Round Bar is outlined in the following table
| Grade | C | Mn | Si | P | S | Cr | Ni | |
|---|---|---|---|---|---|---|---|---|
| 410 | min. max. | - 0.15 | - 1 | - 1 | - 0.04 | - 0.03 | 11.5 13.5 | 0.75 |
A276 410 Round Bar Mechanical and Physical Properties
The mechanical properties of grade A276 410 Round Bar are displayed in the following table.
| Tempering Temperature (°C) | Tensile Strength (MPa) | Yield Strength 0.2% Proof (MPa) | Elongation (% in 50 mm) | Hardness Brinell (HB) | Impact Charpy V (J) |
|---|---|---|---|---|---|
| Annealed * | 480 min | 275 min | 16 min | - | - |
| 204 | 1475 | 1005 | 11 | 400 | 30 |
| 316 | 1470 | 961 | 18 | 400 | 36 |
| 427 | 1340 | 920 | 18.5 | 405 | # |
| 538 | 985 | 730 | 16 | 321 | # |
| 593 | 870 | 675 | 20 | 255 | 39 |
| 650 | 300 | 270 | 29.5 | 225 | 80 |
A276 410 Round Bar Physical Properties
Physical properties of 410 grade stainless steel in the annealed condition
Grade Density (kg/m3) Elastic Modulus (GPa) Mean Coefficient of Thermal Expansion (μm/m/°C) Thermal Conductivity (W/m.K) Specific Heat 0-100 °C (J/kg.K) Electrical Resistivity (nΩ.m) 0-100 °C 0-315 °C 0-538 °C at 100 °C at 500 °C 410 7800 200 9.9 11 11.5 24.9 28.7 460 570