ASTM A240 SS 321 Coil Mechanical Properties

Grade	Tensile Strength (MPa) min	Yield Strength 0.2% Proof (MPa) min	Elongation (% in 50mm) min	Hardness
Rockwell B (HR B) max	Brinell (HB) max
321	515	205	40	95	217

321 Stainless Steel Coil Chemical Compostion and Properties

The chemical composition of grade 321 Stainless Steel is outlined in the following table

Grade	C	Mn	Si	P	S	Cr	Mo	Ni	N	Other
321	min. max	- 0.08	2.00	0.75	0.045	0.030	17.0 19.0	-	9.0 12.0	0.10	Ti=5(C+N) 0.70
321H	min. max	0.04 0.10	2.00	0.75	0.045	0.030	17.0 19.0	-	9.0 12.0	-	Ti=4(C+N) 0.70

#2 - Cold Rolled
# 2BA- Smooth finish produced by cold rolling and bright annealing. A light pass using highly polished rolls produces a glossy finish. A 2BA finish may be used for lightly formed applications where a glossy finish is desired in the formed part. Polished - Various grit finish for specific polish finished requirements.
* Not all finishes are available in all alloys - Contact Ulbrich Sales for more information.

WIRE FINISHES

XC - Extra clean bright annealed or bright annealed and cold rolled Grease - Ultra-bright finish (for decorative applications) Soap - Soap is not removed from tempered wire to act as a lubricant. * Contact Ulbrich Wire for custom wire finishes.