1.4113 steel pipe 434 is one of the most widely used of the "non-hardenable" ferritic stainless steels. The addition of molybdenum increases this 1.4113 steel pipe 434 alloy's corrosion resistance and its attack to many deicing chemicals. 1.4113 steel pipe 434 combines good heat and oxidation resistance up to 1500 °F (816 °C) as well as good mechanical properties.

Sample	Free provided
Sample time	2-3 days
MOQ	1 ton , We can accept sample order.
Package	Standard export seaworthy package, water proof paper + wooden pallet or as required.
Delivery time	Prompt delivery , 7-15 days after deposit, or as the order quantity.
Port of loading	Shanghai,Lianyungang, Tianjin, Ningbo, China
Application	Building, Construction, Food, Industry, Chemistry, Agriculture, Mechanical, Medical, Devices, etc

PHYSICAL PROPERTIES

Density: 0.28 lbs/in3 7.74 g/cm3
Electrical Resistivity: microhm-in (microhm-cm):
68 °F (20 °C): 23.68 (60)

Specific Heat: BTU/lbl°F (kJ/kg•K):
32 - 212 °F (0 - 100 °C): 0.11 (0.46)

Thermal Conductivity: BTU/hr/ft2/ft/° F (W/m•K)
At 212 °F (100 °C): 15.1 (26.1)
At 932 °F (500 °C): 15.2 (26.3)
Mean Coefficient of Thermal Expansion: in/inl° F (µm/m•K):
32 -212 ° F (0 - 100 °C): 5.8 x 10-5 (10.4)
32-1000 ° F (0- 538 °C): 6.3 x 10-5 (11.4)

Hot rolled annealed and descaled. 1.4113 steel pipe 434 is available in strip, foil and ribbon. 1.4113 steel pipe 434 is used for applications where a smooth decorative finish is not required.

Dull finish produced by cold rolling, annealing and descaling. Used for deep drawn parts and those parts that need to retain lubricants in the forming process.

Smooth finish produced by cold rolling, annealing and descaling. A light cold rolling pass is added after anneal with polished rolls giving it a brighter finish than 2D.

1.4113 steel pipe 434