Type 434 pipe stainless steel is readily drawn and formed. Its drawing characteristics are similar to those of low carbon steel, although it is stronger in the annealed condition and will require stronger tooling and increased power. Type 434 pipe stainless steel is also adaptable to most hot-forming operations. Type 434 pipe stainless steel does have a slightly increased tendency to "rope" during forming than Type 430.
| Product Name: | Stainless Steel Tubing/Pipe | Standard: | ASTM, AiSi, ASTM A269, ASTM A213. Etc |
|---|---|---|---|
| Application: | Tubing In Oil ，gas Well，boiler | Grade: | 300 Series, 304/304L/316/316L/321/309S/310S, Etc |
| Heat Treatment: | Bright Annealed | Process Method: | Cold Drawn |
| Inspection: | 100% | Surface Finish: | Bright Annealed/ Polished |
| Certification: | ISO | Tolerance: | According Customer's Requirement |
| Length: | According To The Sizes | Certificates: | ISO9001:2008 & PED |
| NDT: | Eddy Current Or Hydraulic Test Or UT | Packing: | Plywood Case Or Wooden Case |
Specific Heat: BTU/lbl°F (kJ/kg•K):
Specific Heat: BTU/lbl°F (kJ/kg•K):
32 - 212 °F (0 - 100 °C): 0.11 (0.46)
Thermal Conductivity: BTU/hr/ft2/ft/° F (W/m•K)
At 212 °F (100 °C): 15.1 (26.1)
At 932 °F (500 °C): 15.2 (26.3)
Mean Coefficient of Thermal Expansion: in/inl° F (µm/m•K):
32 -212 ° F (0 - 100 °C): 5.8 x 10-5 (10.4)
32-1000 ° F (0- 538 °C): 6.3 x 10-5 (11.4)
Modulus of Elasticity: ksi (MPa)
29 x 103 (200 x 103) in tension
Magnetic Permeability: Magnetic
Melting Range: 2700 - 2790 ° F (1482 - 1532 °C)
Hot Tags: type 434 pipe stainless steel, China, suppliers, manufacturers, factory, buy, price, pricelist, for sale, in stock, free sample