904L gives good resistance to both organic and inorganic acids.The addition of copper in 904L grade gives excellent corrosion resistance against nickel stainless steels, to sulphuric, phosphoric, acetic acids, hydrochloric acids, etc. It also gives a high resistance to pitting in chloride solutions, an excellent resistance to both crevice and stress corrosion cracking
SS 904L Plate Dimension
| Grade | 904L | |
| Density (kg/m3) | 7900 | |
| Elastic Modulus (GPa) | 190 | |
| Mean Co-eff of Thermal Expansion (µm/m/°C) | 0-100°C | 15 |
| 0-315°C | ||
| 0-538°C | ||
| Thermal Conductivity (W/m.K) | At 20°C | 11.5 |
| At 500°C | ||
| Specific Heat 0-100°C (J/kg.K) | 500 | |
| Elec Resistivity (nΩ.m) | 952 | |
904L Stainless Steel Plate Chemical Composition
| Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness Rockwell B (HR B) | Hardness Brinell (HB) |
| 490 | 220 | 36 | 70-90 typical | 150 |
SS 904L Plate Mechanical Properties
| Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness Rockwell B (HR B) | Hardness Brinell (HB) |
| 490 | 220 | 36 | 70-90 typical | 150 |
Material Testing of 904L Plate
1) Mechanical Testing Such as Tensile of Area,
2) Hardness Test,
3) Chemical Analysis – Spectro Analysis,
4) Positive Material Identification – PMI Testing,
5) Flattening Test,
6) Micro and Macro Test,
7) Pitting Resistance Test,
8) Flaring Test,
9) and Intergranular Corrosion (IGC) Test.