B35P135 Grain Oriented Electrical Steel
The primary purpose of adding silicon to the steel is to increase its electrical resistance, which in turn reduces the amount of energy lost as heat during the magnetic induction process.
B35P135 mainly low-carbon steel, requires a good cold bending and welding properties, as well as some of the press performance.
B35P135 steel Mechanical Properties
|
Grade |
Nominal thickness（mm） |
tensile strength L（N/mm2） |
Yield Strength L（N/mm2） |
Elongation L（%） |
Hardness HV1 |
Bending frequency (times) |
Stacking factor（%） |
|
B35P135 |
0.35 |
350 |
310 |
11 |
195 |
17 |
98.0 |
NOTE:.
a detector according to GB / t228-2002, GB / T 19289-2003
b. above are typical values only for reference does not guarantee
c. L direction refers to the rolling direction
B35P135 steel plate/sheet Electromagnetic induction standard
|
Grade |
Nominal thickness（mm） |
Theoretical density（kg/dm3） |
Maximum core loss P17/50 |
minimum magnetic induction B8 |
|
B35P135 |
0.35 |
7.65 |
1.35 |
1.88 |
Hot Tags: b35p135 grain oriented silicon steel, China, suppliers, manufacturers, factory, buy, price, pricelist, for sale, in stock, free sample, magnetic induction, transformer core, Oriented Silicon Steel, good surface quality, Cold Rolled, low iron loss