We are capable of not just producing even large batches of standard as well as non-standard, tailor made of these SS UNS S31000 Pipes and Tubes, but as well specializes in manufacturing critical fasteners. Further, ss 310 Tubes has its pulse on the technological up-gradations and innovations of its upcoming projects. Hence, we are able to cater to its customer’s emerging needs. Heat Treatment of DIN 1.4845 Seamless Pipes and Tubes are solution annealed by heating to temperature range 1040 -1065 Degree C, holding at temperature until thoroughly soaked, and then water quenching. However, AISI 310 Tubes will be sensitised to intergranular corrosion after service at temperatures in range 550 – 800 Deg C. Buy SS 310 Pipes at reasonable cost from us.

310 STAINLESS STEEL PIPE

310 STAINLESS STEEL PIPES CHEMICAL COMPOSITION

The below table shows the chemical composition of the used for Stainless Steel Tube:

Grade	C	Mn	Si	P	S	Cr	Mo	Ni	N
310	min.	–	–	–	–	–	24.0	–	19.0	–
max.	0.25	2.0	1.50	0.045	0.030	26.0	22.0	–

SS 310 PIPE MECHANICAL PROPERTIES

Grade	Tensile Strength (MPa) min	Yield Strength 0.2% Proof (MPa) min	Elongation (% in 50mm) min	Hardness
Rockwell B (HR B) max	Brinell (HB) max
310 – 310S	515	205	40	95	217

STAINLESS STEEL 310 PIPES PHYSICAL PROPERTIES

Grade	Density (kg/m3)	Elastic Modulus (GPa)	Mean Coefficient of Thermal Expansion (m/m/0C)	Thermal Conductivity (W/m.K)	Specific Heat 0-1000C (J/kg.K)	Electrical Resistivity (n.m)
0-1000C	0-3150C	0-5380C	at 1000C	at 5000C
310 – 310S	7750	200	15.9	16.2	17.0	14.2	18.7	500	720