8006 aluminum foil is a special aluminum alloy for container foil products. 8006 aluminium foil adopts hot rolling method and its tensile strength is between 123-135 Mpa. 8006 aluminum foil product reaches the brushing water grade A. The surface is very flat, clean, and free of oil. 8006 aluminium foil is especially suitable for aerospace wrinkle-free lunch boxes. After stamping, the edges could be free of wrinkles and the appearance is smooth and smooth.
Technical Parameter of 8006 Aluminum Foil
| Ingredient | Cu | Mg | Mn | Fe | Si | Zn | Cr | Other | Al |
| Content | ≤0.30 | ≤0.10 | 0.30~1.0 | 1.2~2.0 | ≤0.40 | ≤0.10 | – | 0.15 | Margin |
| Alloy Type | >8006 aluminium foil | ||||||||
| Alloy State | >O, H14, H16, H18, H19, H22, H24, H26, H28 | ||||||||
| Thickness (mm) | >0.014-0.2 | ||||||||
| Width (mm) | >100-1500 | ||||||||
| Length | >Jumbo roll | ||||||||
Strength of CHAL 8006 Aluminum Foil
Technologies: Top polishing technology guarantees good luster and smooth surface.
Markets: Obtain market sharing all over the world.
Equipment: Advanced cutting line to provide a wide range of specifications.
Responsibility: Engaged in charity donation and provide eco-friendly products.
The difference between 8006 aluminum foil and 3003 aluminum foil, 8011 aluminum foil:
1. 8006 lunch box aluminum foil has higher strength; Material is hot rolled.
2. Both 3003 aluminum foil and 8011 aluminium foil have low strength and the material is cold cast.
3. The elongation and cup convex value of 8006 aluminum foil is higher than 8011, 3003 lunch box aluminum foil.
4. The tensile strength of the 8006 container foil is 10 MPa higher than that of the 8011 aluminum foil, which is slightly lower than that of the 3003 aluminum foil.