TYPICAL STANDARDS
| GRADE | SIZES ROUTINELY STOCKED | ||
|---|---|---|---|
| Temper | Thickness (Metric/Imperial) | Width | Length |
| 3105-O | Inquire for sizes | ||
| 3105-H22 | Inquire for sizes | ||
| 3105-H24 | Inquire for sizes | ||
| 3105-H26 | Inquire for sizes | ||
| 3105-H28 | Inquire for sizes |
GENERAL INFO ABOUT 3105 ALUMINUM SHEET
3105 aluminum sheet is 98% pure aluminum with the addition of specific alloys for strength improvement. This alloy can’t be hardened by heat treatment. It has excellent weldability, formability, and corrosion resistance.
MORE DETAILS ABOUT 3105 ALUMINUM SHEET
ADVANTAGES/DISADVANTAGES INDUSTRIES MACHINING WELDING HEAT TREATMENT
Advantages/Disadvantages
It has excellent corrosion resistance and formability. On the other hand, it is not heat-treatable.
CHEMICAL PROPERTIES
| SI | FE | CU | MN | MG | CR | ZN | TI |
|---|---|---|---|---|---|---|---|
| 0.60% | 0.70% | 0.30% | 0.30-0.80% | 0.20-0.80% | 0.20% | 0.40% | 0.10% |
MECHANICAL PROPERTIES
| GRADE | STRENGTH (METRIC/IMPERIAL) | ELONGATION | |
|---|---|---|---|
| Temper | Ultimate Tensile Strength (min - max) | Ultimate Yield Strength | % at 50mm |
| 3105-O | 110-155 MPa / 15,194 - 22,480 psi | - | 16 |
| 3105-H12 | 130-175 MPa / 18,854 - 25,381 psi | 115 MPa / 16,679 psi | 2 |
| 3105-H14 | 160-205 MPa / 23,206 - 29,732 psi | 145 MPa / 21,030 psi | 2 |
| 3105-H16 | 185-230 MPa / 26,831 - 33,358 psi | 170 MPa / 24,656 psi | 1 |
| 3105-H18 | 215 MPa / 31,183 psi | 190 MPa / 27,557 psi | 1 |
FREQUENTLY ASKED QUESTIONS
WHAT IS THE DIFFERENCE BETWEEN 3003 H14 VS 3105 H24? WHAT ARE THE SPECIFICATIONS OF 3105 H24 ALUMINUM? WHAT ARE THE SPECIFICATIONS OF 3105 H14 ALUMINUM? WHAT IS 3105 PAINTED ALUMINUM SHEET?
What is the difference between 3003 H14 vs 3105 H24?
ANSWER:
There are a couple differences between 3003 H14 and 3105 H24. One of them is the Brinell Hardness; 3003 H14 has 42 BHN and 3105 H24 has 47 BHN. Another difference is the Fatigue Strength; 3003 H14 has only 60 MPa, whereas 3105 H24 has 74 MPa. In the alloy composition, 3003 H14 contains more Magnesium than 3105 H24. But 3105 H24 contains a little bit of Titanium, Chromium and Copper that 3003 H14 does not have.